I-Yttrium Aluminium Garnet Engashintshiwe (Y3Al5O12 noma i-YAG) iwuphawu oluncane olusha kanye nezinto ezibonakalayo ezingasetshenziselwa kokubili i-UV ne-IR optics.Iwusizo ikakhulukazi ekusetshenzisweni kwezinga lokushisa eliphezulu kanye namandla aphezulu.Ukuzinza komshini namakhemikhali kwe-YAG kuyafana nalokho kweSapphire.
Izinzuzo ze-YAG Engasusiwe:
• High conductivity ezishisayo, izikhathi 10 kangcono kunezibuko
• Iqinile kakhulu futhi ihlala isikhathi eside
• Ukungabi ne-birefringence
• Izakhiwo ezizinzile zemishini namakhemikhali
• Umkhawulo omkhulu womonakalo omkhulu
• Inkomba ephezulu ye-refraction, esiza idizayini yelensi ehlehla kancane
Izici:
• Ukudluliselwa ngo-0.25-5.0 mm, akukho ukumuncwa ku-2-3 mm
• High conductivity ezishisayo
• Inkomba ephezulu ye-refraction kanye ne-Non-birefringence
Izici eziyisisekelo:
Igama Lomkhiqizo | Kuhlehliswe i-YAG |
Isakhiwo sekristalu | I-Cubic |
Ukuminyana | 4.5g/cm3 |
Ibanga Lokudlulisela | 250-5000nm |
I-Melting Point | 1970°C |
Ukushisa Okuthize | 0.59 Ws/g/K |
I-Thermal Conductivity | 14 W/m/K |
I-Thermal Shock Resistance | 790 W/m |
Ukunwetshwa kwe-Thermal | 6.9×10-6/K |
dn/dt, @633nm | 7.3×10-6/K-1 |
Mohs Ukuqina | 8.5 |
I-Refractive Index | 1.8245 @0.8mm, 1.8197 @1.0mm, 1.8121 @1.4mm |
Amapharamitha wezobuchwepheshe:
Ukuqondisa | [111] phakathi kuka-5° |
Ububanzi | +/-0.1mm |
Ubukhulu | +/-0.2mm |
Ukucaba | l/8@633nm |
Ukufana | ≤30″ |
I-Perpendicularity | ≤ 5′ |
Scratch-Dig | 10-5 nge-MIL-O-1383A ngayinye |
I-Wavefront Distortion | kangcono kune-l/2 intshi ngayinye@1064nm |