Ho: YAG Ho3+ama-ion afakwe kumakristalu e-laser avikelayo abonise amashaneli e-laser ahlukahlukene ayi-14, asebenza ngezindlela zesikhashana ukusuka ku-CW kuya kumodi ekhiyiwe.I-Ho:YAG ijwayele ukusetshenziswa njengendlela ephumelelayo yokukhiqiza ukukhishwa kwe-laser okungu-2.1-μm kusuka ku-5I7-5I8inguquko, yezinhlelo zokusebenza ezifana ne-laser remote sensing, ukuhlinzwa kwezokwelashwa, kanye nokumpompa ama-Mid-IR OPO's ukuze kuzuzwe ukukhishwa kwe-3-5micron.I-Direct diode pumped systems, kanye ne-Tm: I-Fiber Laser pumped system ibonise ukusebenza kahle kwe-slope, ezinye zisondela emkhawulweni wethiyori.
Izakhiwo Eziyisisekelo
Ibanga lokuhlushwa le-Ho3+ | 0.005 - 100 i-athomu% |
I-Emission Wavelength | 2.01 um |
I-Laser Transition | 5I7→5I8 |
I-Flouresence Lifetime | 8.5 ms |
Iphampu Wavelength | 1.9 um |
I-Coefficient of Thermal Expansion | 6.14 x 10-6 K-1 |
I-Thermal Diffusivity | 0.041 cm2 s-2 |
I-Thermal Conductivity | 11.2 W m-1 K-1 |
Ukushisa Okuthile (Cp) | 0.59 J g-1 K-1 |
I-Thermal Shock Resistant | 800W m-1 |
I-Refractive Index @ 632.8 nm | 1.83 |
I-Melting Point | 1965℃ |
Ukuminyana | 4.56g cm-3 |
Ukuqina kwe-MOHS | 8.25 |
I-Modulus Encane | 335 gp |
Isakhiwo Sekristalu | I-Cubic |
Umumo Ojwayelekile | <111> |
I-Y3+ Site Symmetry | D2 |
I-Lattice Constant | a=12.013 Å |
Imingcele Yezobuchwepheshe
Ukuhlanekezela kwe-Wavefront | L/8 per intshi @633nm |
Isilinganiso sokuqedwa | > 28dB |
Ukuhlanekezela kwe-Wavefront | L/8 per intshi @633nm |
Isilinganiso sokuqedwa | > 28dB |
Ukubekezelelana:Izinduku ezinobubanzi | (+0,-0.05)mm,( ±0.5) mm |
Ikhwalithi yobuso | 10/5 Scratch/dig nge-MIL-O-1380A ngayinye |
Ukufana | <10arc amasekhondi |
I-Perpendicularity | <5 arc amaminithi |
Imbobo | >90% |
Ukucaba | λ/10@ 633 nm |
Ukubekezelelana:Izinduku ezinobubanzi | (+0,-0.05)mm,( ±0.5) mm |
Ikhwalithi yobuso | 10/5 Scratch/dig nge-MIL-O-1380A ngayinye |
Ukufana | <10arc amasekhondi |
I-Perpendicularity | <5 arc amaminithi |
Imbobo | >90% |
Ukucaba | λ/10@ 633 nm |